+ + CDA C93600 High Leaded Tin Bronze
CDA C93600 High Leaded Tin Bronze

C93600 High Leaded Tin Bronze

  • Bronze C93600: High Leaded Tin Bronze
  • Solids: 1/2" to 13" OD
  • Tubes: 1" to 16" OD
  • Rectangles: Up to 20"
  • Standard Lengths: 144"
 

Similar or Equivalent Specification

CDAASTMASARCONSAEAMSFederalIngot#MilitaryOther Desc
C93600 B505              

Chemical Composition (according to ASTM B505-08)

Cu%Sn%Pb%Zn%Fe%Ni%Sb%P%S%Al%Mn%Si%
Note: Single values represent maximums.
79.00-83.00 6.00-8.00 11.00-13.00 1.00 0.20 1.00 0.55 1.5 0.08 0.005 N/A 0.005

Mechanical Properties (according to ASTM B505-08)

Tensile Strength (min)Yield Strength (at .5% extention under load min)Elongation (in 2in. or 50mm min, %)Brinell Hardness (min)Remarks
KsiMPaKsiMPa   
33 227 20 138 10    

Machinability

AlloyRatingDensity
C93600 80 0.325

Physical Properties (provided by CDA)

 US CustomaryMetric
Melting Point - Liquidus 1720 F 938 C
Melting Point - Solidus 1550 F 843 C
Density 0.325 lb/in3 at 68 F 9.0 gm/cm3 @ 20 C
Specific Gravity 90 9.0
Electrical Conductivity 11 %IACS @ 68 F 0.064 MegaSiemens/cm @ 20 C
Thermal Conductivity 28.50 Btu · ft/(hr · ft2·°F)at 68F 49.36 W/m · °K at 20 C
Coefficient of Thermal Expansion 10.30 ·10-6 per oF (68-392 F) 18.54 ·10-6 per °C (20-200 C)
Specific Heat Capacity 0.090 Btu/lb/°F at 68 F 377.1 J/kg · °K at 293 K
Modulas of Elasticity in Tension 14000 ksi 96516 MPa

Fabrication Properties (provided by CDA)

Joining TechniqueSuitability
Soldering Good
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended

Thermal Properties (provided by CDA)

TreatmentTemp./Time - USTemp./Time - SI
Stress Temperature 500 260
Solution Minimum    
Solution Maximum    
Solution Time 0.0
Solution Medium None
Precipitation Value    
Precipitation Time    
Precipitation Medium None
Annealing Minimum    
Annealing Maximum    
Annealing Time  
Hot Works Minimum    
Hot Works Maximum