C95300 Aluminum Bronze
C95300 Aluminum Bronze
- Bronze C95300: C95300 Aluminum Bronze
- Solids: 1/2" to 9" OD
- Tubes: 1 1/8" to 9" OD
- Rectangles: Up to 15"
- Standard Lengths: 144"
Similar or Equivalent Specification
| CDA | ASTM | ASARCON | SAE | AMS | Federal | Ingot# | Military | Other Desc |
|---|---|---|---|---|---|---|---|---|
| C95300 | B505 | 68B | QQ-C-390B TYPE III | 415 | MIL-B-16033 CLASS 2 | ALUMINUM BRONZE 9B | ||
| J461 | QQ-B-671 CLASS 2 | |||||||
| J462 |
Chemical Composition (according to ASTM B505-08)
| Cu% | Sn% | Pb% | Zn% | Fe% | Ni% | Sb% | P% | S% | Al% | Mn% | Si% |
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Note: Single values represent maximums.
|
|||||||||||
| 86.00 min | N/A | N/A | N/A | 0.80-1.50 | N/A | N/A | N/A | N/A | 9.00-11.00 | N/A | N/A |
Mechanical Properties (according to ASTM B505-08)
| Tensile Strength (min) | Yield Strength (at .5% extention under load min) | Elongation (in 2in. or 50mm min, %) | Brinell Hardness (min) | Remarks | ||
|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | |||
| 70 | 483 | 26 | 179 | 25 | N/A | |
Machinability
| Alloy | Rating | Density |
|---|---|---|
| C95300 | 55 | 0.272 |
Physical Properties (provided by CDA)
| US Customary | Metric | |
|---|---|---|
|
||
| Melting Point - Liquidus | 1913 F | 1045 C |
| Melting Point - Solidus | 1904 F | 1040 C |
| Density | 0.272 lb/in3 at 68 F | 7.53 gm/cm3 @ 20 C |
| Specific Gravity | 7.530 | 7.53 |
| Electrical Resistivity | 80.20 ohms-cmil/ft @ 68 F | 13.33 microhm-cm @ 20 C |
| Electrical Conductivity | 13 %IACS @ 68 F | 0.075 MegaSiemens/cm @ 20 C |
| Thermal Conductivity | 36.30 Btu · ft/(hr · ft2·°F)at 68F | 62.8 W/m · °K at 20 C |
| Coefficient of Thermal Expansion | 9 ·10-6 per oF (68-392 F) | 16.2 ·10-6 per °C (20-200 C) |
| Specific Heat Capacity | 0.090 Btu/lb/°F at 68 F | 377.1 J/kg · °K at 293 K |
| Modulas of Elasticity in Tension | 16000 ksi | 110000 MPa |
| Magnetic Permeability* | 1.070 | 1.07 |
Fabrication Properties (provided by CDA)
| Joining Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Good |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Excellent |
| Coated Metal Arc Welding | Good |
Thermal Properties (provided by CDA)
| Treatment | Temp./Time - US | Temp./Time - SI |
|---|---|---|
| Stress Temperature | 600 | 316 |
| Solution Minimum | 1585 | 863 |
| Solution Maximum | 1635 | 891 |
| Solution Time | 1.0 | |
| Solution Medium | Water | |
| Precipitation Value | ||
| Precipitation Time | ||
| Precipitation Medium | Water | |
| Annealing Minimum | 1150 | 622 |
| Annealing Maximum | 1225 | 663 |
| Annealing Time | 1.0 | |
| Hot Works Minimum | ||
| Hot Works Maximum | ||