C94300 High Leaded Tin Bronze
C94300 High Leaded Tin Bronze
- Bronze C94300: C94300 High Leaded Tin Bronze
- Solids: 1/2" to 10" OD
- Tubes: 1" to 16" OD
- Rectangles: Up to 10"
- Standard Lengths: 144"
Similar or Equivalent Specification
CDA | ASTM | ASARCON | SAE | AMS | Federal | Ingot# | Military | Other Desc |
C94300 |
B505 |
|
|
|
QQ-C-390B TYPE III |
|
MIL-B-16261 GRADE V |
|
Chemical Composition (according to ASTM B505-08)
Cu% | Sn% | Pb% | Zn% | Fe% | Ni% | Sb% | P% | S% | Al% | Mn% | Si% |
Note: Single values represent maximums.
|
67.00-72.00 |
4.50-6.00 |
23.00-27.00 |
0.80 |
0.15 |
1.00 |
0.80 |
1.50 |
0.08 |
0.005 |
N/A |
0.005 |
Mechanical Properties (according to ASTM B505-08)
Tensile Strength (min) | Yield Strength (at .5% extention under load min) | Elongation (in 2in. or 50mm min, %) | Brinell Hardness (min) | Remarks |
Ksi | MPa | Ksi | MPa | | | |
21 |
145 |
15 |
103 |
7 |
N/A |
|
Machinability
Alloy | Rating | Density |
C94300 |
80 |
0.336 |
Physical Properties (provided by CDA)
| US Customary | Metric |
Incipient Melting |
600 F |
316 C |
Density |
0.336 lb/in3 at 68 F |
9.3 gm/cm3 @ 20 C |
Specific Gravity |
9.300 |
9.3 |
Electrical Resistivity |
113.50 ohms-cmil/ft @ 68 F |
18.87 microhm-cm @ 20 C |
Electrical Conductivity |
9 %IACS @ 68 F |
0.053 MegaSiemens/cm @ 20 C |
Thermal Conductivity |
36.20 Btu · ft/(hr · ft2·°F)at 68F |
62.7 W/m · °K at 20 C |
Specific Heat Capacity |
0.090 Btu/lb/°F at 68 F |
377.1 J/kg · °K at 293 K |
Modulas of Elasticity in Tension |
10500 ksi |
72400 MPa |
Magnetic Permeability |
1 |
1.0 |
Fabrication Properties (provided by CDA)
Joining Technique | Suitability |
Soldering |
Good |
Brazing |
Poor |
Oxyacetylene Welding |
Not Recommended |
Gas Shielded Arc Welding |
Not Recommended |
Coated Metal Arc Welding |
Not Recommended |
Thermal Properties (provided by CDA)
Treatment | Temp./Time - US | Temp./Time - SI |
Stress Temperature |
500 |
260 |
Solution Minimum |
|
|
Solution Maximum |
|
|
Solution Time |
0.0 |
Solution Medium |
None |
Precipitation Value |
|
|
Precipitation Time |
|
|
Precipitation Medium |
None |
Annealing Minimum |
|
|
Annealing Maximum |
|
|
Annealing Time |
|
Hot Works Minimum |
|
|
Hot Works Maximum |
|
|