C93500 High Leaded Tin Bronze
C93500 High Leaded Tin Bronze
- Bronze C93500: High Leaded Tin Bronze
- Solids: 1/2" to 13" OD
- Tubes: 1" to 16" OD
- Rectangles: Up to 20"
- Standard Lengths: 144"
Similar or Equivalent Specification
| CDA | ASTM | ASARCON | SAE | AMS | Federal | Ingot# | Military | Other Desc |
|---|
| C93500 |
B505 |
59 |
66 |
|
QQ-C-390 B TYPE III |
326 |
MIL-B-11553 COMP. 14 |
|
Chemical Composition (according to ASTM B505-08)
| Cu% | Sn% | Pb% | Zn% | Fe% | Ni% | Sb% | P% | S% | Al% | Mn% | Si% |
|---|
|
Note: Single values represent maximums.
- † In determining copper minimum, copper may be calculated as copper plus nickel.
|
| 83.00-86.00 |
4.30-6.00 |
8.00-10.00 |
2.00 |
0.20 |
1.00† |
0.30 |
1.5 |
0.08 |
0.005 |
N/A |
0.005 |
Mechanical Properties (according to ASTM B505-08)
| Tensile Strength (min) | Yield Strength (at .5% extention under load min) | Elongation (in 2in. or 50mm min, %) | Brinell Hardness (min) | Remarks |
|---|
| Ksi | MPa | Ksi | MPa | | | |
|---|
| 30 |
207 |
16 |
110 |
12 |
|
|
Machinability
| Alloy | Rating | Density |
|---|
| C93500 |
70 |
0.320 |
Physical Properties (provided by CDA)
| | US Customary | Metric |
|---|
| Melting Point - Liquidus |
1830 F |
999 C |
| Melting Point - Solidus |
1570 F |
854 C |
| Incipient Melting |
600 F |
316 C |
| Density |
0.320 lb/in3 at 68 F |
8.86 gm/cm3 @ 20 C |
| Specific Gravity |
8.860 |
8.86 |
| Electrical Resistivity |
- 68.40 ohms-cmil/ft @ 68 F
|
11.36 microhm-cm @ 20 C |
| Electrical Conductivity |
15 %IACS @ 68 F |
0.088 MegaSiemens/cm @ 20 C |
| Thermal Conductivity |
40.70 Btu · ft/(hr · ft2·°F)at 68F |
70.4 W/m · °K at 20 C |
| Coefficient of Thermal Expansion |
9.90 ·10-6 per oF (68-392 F) |
17.8 ·10-6 per °C (20-200 C) |
| Specific Heat Capacity |
0.090 Btu/lb/°F at 68 F |
377.1 J/kg · °K at 293 K |
| Modulas of Elasticity in Tension |
14500 ksi |
10000 MPa |
| Magnetic Permeability |
1 |
1.0 |
Fabrication Properties (provided by CDA)
| Joining Technique | Suitability |
|---|
| Soldering |
Good |
| Brazing |
Good |
| Oxyacetylene Welding |
Not Recommended |
| Gas Shielded Arc Welding |
Not Recommended |
| Coated Metal Arc Welding |
Not Recommended |
Thermal Properties (provided by CDA)
| Treatment | Temp./Time - US | Temp./Time - SI |
|---|
| Stress Temperature |
500 |
260 |
| Solution Minimum |
|
|
| Solution Maximum |
|
|
| Solution Time |
0.0 |
| Solution Medium |
None |
| Precipitation Value |
|
|
| Precipitation Time |
|
|
| Precipitation Medium |
None |
| Annealing Minimum |
|
|
| Annealing Maximum |
|
|
| Annealing Time |
|
| Hot Works Minimum |
|
|
| Hot Works Maximum |
|