C91100 High Tin Bronze
C91100 High Tin Bronze
- Bronze C91100: High Tin Bronze
- Solids: 1" to 6" OD
- Tubes: 1" to 6" OD
- Rectangles: Up to 10"
- Standard Lengths: 144"
Similar or Equivalent Specification
| CDA | ASTM | ASARCON | SAE | AMS | Federal | Ingot# | Military | Other Desc |
|---|---|---|---|---|---|---|---|---|
| C91100 | ASTM B22 | N/A | N/A | N/A | N/A | N/A | N/A | Sand |
Chemical Composition (according to ASTM B505-08)
| Cu% | Sn% | Pb% | Zn% | Fe% | Ni% | Sb% | P% | S% | Al% | Mn% | Si% |
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Note: Single values represent maximums.
|
|||||||||||
| 82.00-85.00 | 15.00-17.00 | 0.25 | 0.25 | 0.25 | 0.50A | 0.20 | 1.0 | 0.05 | 0.005 | N/A | 0.005 |
Mechanical Properties (according to ASTM B505-08)
| Tensile Strength (min) | Yield Strength (at .5% extention under load min) | Elongation (in 2in. or 50mm min, %) | Brinell Hardness (min) | Remarks | ||
|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | |||
| N/A | N/A | N/A | N/A | N/A | 160 (3000 kg) | |
Machinability
| Alloy | Rating | Density |
|---|---|---|
| C91100 | 10 | 0.318 |
Physical Properties (provided by CDA)
| US Customary | Metric | |
|---|---|---|
| Melting Point - Liquidus | 1742 F | 950 C |
| Melting Point - Solidus | 1505 F | 818 C |
| Electrical Resistivity | 122.80 ohms-cmil/ft @ 68 F | 20.41 microhm-cm @ 20 C |
| Electrical Conductivity | 8 %IACS @ 68 F | 0.049 MegaSiemens/cm @ 20 C |
| Specific Heat Capacity | 0.090 Btu/lb/°F at 68 F | 377.1 J/kg · °K at 293 K |
| Modulas of Elasticity in Tension | 15000 ksi | 103400 MPa |
Fabrication Properties (provided by CDA)
| Joining Technique | Suitability |
|---|---|
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Fair |
Thermal Properties (provided by CDA)
| Treatment | Temp./Time - US | Temp./Time - SI |
|---|---|---|
| Stress Temperature | 500 | 260 |
| Solution Minimum | ||
| Solution Maximum | ||
| Solution Time | 0.0 | |
| Solution Medium | None | |
| Precipitation Value | ||
| Precipitation Time | ||
| Precipitation Medium | None | |
| Annealing Minimum | ||
| Annealing Maximum | ||
| Annealing Time | ||
| Hot Works Minimum | ||
| Hot Works Maximum | ||